When added to aluminium, scandium substantially lowers the rate of recrystallization and associated grain-growth in weld heat-affected zones. Aluminium, being a face-centred-cubic metal, is not particularly subject to the strengthening effects of the decrease in grain diameter. However, the presence of fine dispersions of Al3Sc does increase strength by a small measure, much as any other precipitate system in aluminium alloys. It is added to aluminium alloys primarily to control that otherwise excessive grain growth in the heat-affected zone of weldable structural aluminium alloys, which gives two knock-on effects; greater strengthening via finer precipitation of other alloying elements and by reducing the precipitate-free zones that normally exist at the grain boundaries of age-hardening aluminium alloys.
The original use of scandium-aluminium alloys was in the nose cones of some USSR submarine-launched ballistic missiles (SLBMs). The strength of the resulting nose cone was enough to enable it to pierce the ice-cap without damage, and so, enabling a missile launch while still submerged under the Arctic ice cap.