I spent 9 years machineing PM parts in a powder metal plant. It may be possible to case harden PM parts I don't know. The only reasons to case harden are for better wear with cheaper material, to keep the soft core for better shock resist, or looks. The only one you will get that info from is a S&W enginer that is if it is not a compeny secret.