Is there a question in there? If you used your 586 as indicated I find it hard to believe that you had much, if any, forcing cone erosion. Are you sure you weren't looking at carbon and lead deposit build-up in the FC area? It could also depend on the powder and bullet weight you used - fast burning powders and light bullets can increase the rate of erosion.