Rusty 36 no dash
One of the guys in my squad brought in an old Model 36 that he’s had in, let’s say, storage. It appears to function fine, but it’s rusted.
What do you experienced members think are the chances this gun can be cleaned up? Suggestions requested... thanks!
__________________
Stay Safe...
jd SWCA #3276
|
04-07-2018, 01:39 PM
|
Member
|
|
|
Join Date: Apr 2007
Location: Virginia
Posts: 8,764
Likes: 19,495
Liked 11,856 Times in 5,386 Posts
|
|
Stored in a wet sock?
I bet it is pretty badly pitted.
|
The Following User Likes This Post:
|
|
04-07-2018, 01:50 PM
|
|
Member
|
|
|
Join Date: Apr 2011
Location: Where this month?
Posts: 3,604
Likes: 264
Liked 4,215 Times in 1,714 Posts
|
|
Quote:
Originally Posted by demkofour
What do you experienced members think are the chances this gun can be cleaned up? Suggestions requested... thanks!
|
Depends on what you are expecting?
It will "NEVER" look "GOOD" again. Functional.. not pretty.
|
The Following User Likes This Post:
|
|
04-07-2018, 01:53 PM
|
|
SWCA Member
|
|
|
Join Date: Aug 2016
Location: Virginia
Posts: 326
Likes: 58
Liked 802 Times in 172 Posts
|
|
That’s my kind of project. Love those...
|
The Following 2 Users Like Post:
|
|
04-07-2018, 02:02 PM
|
|
SWCA Member
|
|
|
Join Date: Jul 2012
Posts: 2,477
Likes: 3,790
Liked 3,912 Times in 1,196 Posts
|
|
I sold a friend a 30-1 that was in similar condition (cheap). He had it parkerized/duracoated in a two tone - black frame and gray cylinder. It turned out really nice.
|
04-07-2018, 03:21 PM
|
|
Member
|
|
|
Join Date: Jan 2007
Location: Sandy Utah
Posts: 8,729
Likes: 1,584
Liked 8,865 Times in 3,536 Posts
|
|
Looks like he had it "stored" in the spare tire well of his trunk that leaked when it rained!
__________________
Gunsmithing since 1961
|
The Following 3 Users Like Post:
|
|
04-07-2018, 08:17 PM
|
Member
|
|
|
Join Date: Aug 2014
Location: West Texas
Posts: 2,447
Likes: 5,289
Liked 3,903 Times in 1,519 Posts
|
|
Quote:
Originally Posted by Alk8944
Looks like he had it "stored" in the spare tire well of his trunk that leaked when it rained!
|
Where ever it was stored, it didn't get inspected for a pretty long while. Letting a gun get in that shape oughta be against the law!
Some of those pits are as big as a caliche pit!
__________________
So long ... Ken
|
The Following User Likes This Post:
|
|
04-07-2018, 08:50 PM
|
Junior Member
|
|
|
Join Date: Dec 2013
Location: MA
Posts: 7,707
Likes: 13,905
Liked 9,470 Times in 4,391 Posts
|
|
That's pretty bad. Coincidentally, I've been looking for a "used & abused" (probably with a little surface rust) pre-IL S&W revolver as a candidate for a refinishing project. But I'm mainly interested in one needing a little clean-up, TLC, polishing and re-bluing... not a serious metal restoration project.
I guess it all depends on how much the OP's friend wants to spend. Almost anything can be saved, but at what cost?
|
The Following User Likes This Post:
|
|
04-07-2018, 09:14 PM
|
|
Member
|
|
|
Join Date: May 2012
Location: Texas
Posts: 1,000
Likes: 259
Liked 636 Times in 317 Posts
|
|
Naval jelly is fairly cheap. I'd put some on the rust and see if I could get a better looking at the pitting. IMHO it's past the point of being able to save the original finish. If it were mine I'd strip the finish and remove/fill the pitting as necessary and refinish.
|
The Following User Likes This Post:
|
|
04-07-2018, 11:43 PM
|
|
Member
|
|
|
Join Date: Oct 2008
Location: Denver, CO
Posts: 1,813
Likes: 167
Liked 979 Times in 490 Posts
|
|
Sad to see. Maybe try bead blasting or aomething and re-bluing, but I don’t think it will ever look good.
|
04-08-2018, 09:42 AM
|
Member
|
|
|
Join Date: Sep 2005
Posts: 7,748
Likes: 1,642
Liked 9,151 Times in 3,380 Posts
|
|
That could be restored/refinished.
Worth it to do? Depends on what the gun means to you,,wether you are doing the work yourself as a project or have to pay some one else to do it,,ect.
Yes it can be brought back IMO.
Pitting is just that. It ain't going away by just splashing it with something or covering it with a coating. You have to file , grind or otherwise remove the surrounding metal to a level lower than the deepest pitting.
Other option in welding in some of the deepest pits so as not to have to take the original surface down as far to get a clean one.
You'll probably remove some of the markings, so figure they'll have to be re-cut after polishing is done. Some engravers do that work some don't want to touch it. A roll die would be nice but not many have such along with the other proper caliber, address and misc frame marking dies needed.
If the bore and/or chambers are effected by the pitting in any way like the outside of the gun, I wouldn't put much work in to bringing it back. It'll always be a nice gun w/a rotten bore after that.
Making it into a presentable shooter/carry gun would be an option for it. Much less work and not as much attention to detail towards a restoration.
Just make it look better,,it sounds like it functions just fine as is.
It's perfect piece for someone to work on that is learning the trade of restoration. You can't learn from just reading books and watching YouTube videos.
You spend countless hours at the bench producing a fine finished product that nets nearly nothing in $$ when and if sold. But the experience you gain is priceless.
Not many places to get paid to learn this stuff.
Just my .02,,,
|
The Following 3 Users Like Post:
|
|
04-08-2018, 03:30 PM
|
|
Member
|
|
|
Join Date: Apr 2006
Posts: 17,800
Likes: 7,843
Liked 25,709 Times in 8,687 Posts
|
|
Disassemble, soak in Kroil, clean, and send out to be professionally refinished. It's possible that even after all that, some pitting may still be evident. That's pretty far gone! May not actually pay since the money, effort & time might just not justify the expense.
Last edited by chief38; 04-08-2018 at 05:33 PM.
|
04-08-2018, 04:21 PM
|
SWCA Member
|
|
|
Join Date: Apr 2007
Location: Pennsylvania
Posts: 6,634
Likes: 638
Liked 6,872 Times in 2,546 Posts
|
|
That is just ridiculous.
|
The Following User Likes This Post:
|
|
04-08-2018, 04:47 PM
|
|
Member
|
|
|
Join Date: Oct 2008
Location: Denver, CO
Posts: 1,813
Likes: 167
Liked 979 Times in 490 Posts
|
|
Forgot to add, if the outside is that bad, be prepared for some work on the inside, as well.
|
The Following User Likes This Post:
|
|
04-08-2018, 05:25 PM
|
|
Member
|
|
|
Join Date: Feb 2011
Location: Central PA
Posts: 4,557
Likes: 8,212
Liked 11,453 Times in 3,023 Posts
|
|
Just a thought, and I figured this might be a good post to throw it out there.
Back in the day, lead was used for body work / repairs on car sheetmetal. Would filling the cleaned out pitting with lead, then smoothing and coating with something like Dura Coat work? I realize lead would not hold up to high heat (probably not a concern in a snub revolver), and would be softer than the surrounding metal. Might stand up to careful use, and offer a relatively easy restored look? Just thinking outside the box.
Larry
Last edited by Fishinfool; 04-08-2018 at 05:26 PM.
|
04-08-2018, 08:19 PM
|
Vendor
|
|
|
Join Date: Jan 2010
Location: Kansas City area
Posts: 6,172
Likes: 54,223
Liked 13,580 Times in 4,278 Posts
|
|
Come on, guys, that'll buff out, what's the big deal?
OK, maybe it won't. Still probably a serviceable piece once cleaned up.
|
04-08-2018, 10:46 PM
|
|
US Veteran
|
|
|
Join Date: Apr 2005
Location: Houston, TX
Posts: 101
Likes: 68
Liked 68 Times in 28 Posts
|
|
Quote:
Originally Posted by Fishinfool
Just a thought, and I figured this might be a good post to throw it out there.
Back in the day, lead was used for body work / repairs on car sheetmetal. Would filling the cleaned out pitting with lead, then smoothing and coating with something like Dura Coat work? I realize lead would not hold up to high heat (probably not a concern in a snub revolver), and would be softer than the surrounding metal. Might stand up to careful use, and offer a relatively easy restored look? Just thinking outside the box.
Larry
|
I think I'd try something like J-B Weld or Devcon Plastic Steel to fill in the large/deep pits before I would try lead. Once it's sanded level with the surface and smoothed down, a matte finish with Cerakote or Durakote might not look too bad.
My major concern would be the condition of the bore and chambers.
|
04-09-2018, 06:20 AM
|
Member
|
|
|
Join Date: Jan 2006
Posts: 448
Likes: 157
Liked 228 Times in 113 Posts
|
|
Hurts me to look at it
|
04-09-2018, 08:36 AM
|
Member
|
|
|
Join Date: Sep 2005
Posts: 7,748
Likes: 1,642
Liked 9,151 Times in 3,380 Posts
|
|
It was common practice by the firearms factories to save frames and other parts that came through production and finishing with flaws in them by filling those surface flaws with braze. The surfaces then repolished to level the imperfections.
Then the pistol would be given a nickel plate finish which would nicely cover both the steel base metal and the braze filler.
That was then,,black powder days and all that. Perhaps very early smokeless powder use.
On a modern firearm, that much heat overall is frowned upon but I have seen it done.
Low temp hard solder (used to commonly be called silver solder) is another option. Some flow at around 1000F+/-.
Still alot of heat to play onto the frame, but less than brazing temp up at around 1600F.
You can filll with one of the new tin/silver soft solders. They melt at around 400F. They take plating very nicely just as brass filler does. Just not as hard of a surface as brass. I've used it before for this very reason on small parts and it works well.
This is the same idea as using lead as already suggested as a filler.
The silver/tin soft solder will take plating though where as lead/tin solders or plain lead filler won't generally.
All this braze, hard solder and silver/tin soft solder stuff is of course if you are considering a plated finish to recover the revolvers looks.
I'd take it down as far as possible to remove the pitting. Any left I'd fill with tiny steel inlays, but I do that all the time anyway.
The other method generally used is to dot those small pits left over with TIG or Laser welding and then complete the polishing.
Just some more options as they say..
|
The Following 2 Users Like Post:
|
|
04-09-2018, 08:45 AM
|
|
Moderator
|
|
|
Join Date: Jun 2007
Posts: 26,884
Likes: 981
Liked 18,996 Times in 9,296 Posts
|
|
Many good ideas above. If it is mechanically sound, I think I'd be inclined to remove the rust, then either go "low" (coating) or "high" (hard chrome or full restoration, which S & W would take on, probably). Kind of depends on what your buddy wants in the end.
__________________
Alan
SWCA LM 2023, SWHF 220
|
04-09-2018, 10:29 AM
|
|
Member
|
|
|
Join Date: Oct 2008
Location: Denver, CO
Posts: 1,813
Likes: 167
Liked 979 Times in 490 Posts
|
|
Like they say in the racing industry, “Speed costs money, how fast do you want to go?”
|
The Following User Likes This Post:
|
|
04-09-2018, 12:28 PM
|
Member
|
|
|
Join Date: Nov 2010
Posts: 596
Likes: 34
Liked 247 Times in 117 Posts
|
|
That poor gun. I once went into a LGS and saw what looked like a pristine Colt Python snubby in a velvet lined Colt display box for $200. Couldn't believe my eyes. Asked the clerk about it and he handed the gun to me. The hidden side was COMPLETELY rusted - so much so the cylinder bolt notches were gone!. The box got wet and the gun sat in it for years in a basement until the owners widow found it.
|
04-09-2018, 05:34 PM
|
|
Member
|
|
|
Join Date: Jan 2007
Location: York County, VA
Posts: 3,780
Likes: 0
Liked 4,921 Times in 1,816 Posts
|
|
That is such a waste of a fine firearm. Somebody ought to take that gun and beat him with it.
__________________
Why duck?? It's a 9mm!
|
04-09-2018, 07:37 PM
|
Member
|
|
|
Join Date: Nov 2012
Posts: 1,787
Likes: 1,087
Liked 4,105 Times in 1,168 Posts
|
|
I've purchased plenty of guns in similar conditions. Just tell your guy to take care of the active rust then use it as a beater. If you spend a lot of time outdoors it's nice to have something you don't mind getting bumped around and generally abused.
It will never be brought back to "good" condition, and 36s are cheap enough that if he wants a good looking one he'd be better off killing the active rust then selling it for $200 or so towards a nicer one. Unless you're already set up to do a refinish throwing money at having someone do that is just tossing it away.
|
|