08-29-2020, 07:55 PM
|
Member
|
|
|
Join Date: Aug 2016
Posts: 131
Likes: 6
Liked 65 Times in 29 Posts
|
|
How can I tell a Forged Trigger from a MIM ( N Frame)
Hi,
Just wondering how I can tell a forged case hardened Trigger for a N frame from a MIM Trigger?
|
The Following User Likes This Post:
|
|
08-29-2020, 08:09 PM
|
|
Member
|
|
|
Join Date: Apr 2009
Posts: 6,315
Likes: 13,115
Liked 12,802 Times in 4,228 Posts
|
|
Not sure if it applies to N-frames, but in general I believe the forged triggers are solid, while MIM triggers have a groove along the backside of the trigger.
|
The Following 4 Users Like Post:
|
|
08-29-2020, 09:14 PM
|
|
Member
|
|
|
Join Date: Nov 2013
Location: Spokane, WA
Posts: 13,516
Likes: 1,178
Liked 18,470 Times in 7,307 Posts
|
|
Forged case hardened will have a mottled blue finish with hints of rainbow colors - as long as it hasn't been polished.
MIM will be a very uniform near-black color.
Or at least that is what I have seen consistently.
__________________
Send lawyers, guns & money...
|
The Following User Likes This Post:
|
|
08-29-2020, 09:23 PM
|
|
Member
|
|
|
Join Date: Jul 2017
Location: Pittsburgh PA
Posts: 1,764
Likes: 1,648
Liked 3,117 Times in 1,014 Posts
|
|
Besides the solid trigger back a forged trigger will have sharper lines. Once you see enough of each it’s easy to tell what is what from just a side picture
__________________
-Matt
|
The Following User Likes This Post:
|
|
08-30-2020, 01:59 PM
|
Member
|
|
|
Join Date: Apr 2007
Location: Virginia
Posts: 8,761
Likes: 19,486
Liked 11,854 Times in 5,384 Posts
|
|
Forged hammers look like this:
MIM hammers look like this:
__________________
VCDL, GOA, NRA
|
The Following 11 Users Like Post:
|
JohnHL, LB001, martyd, Mike, SC Hunter, Muley Gil, NY-1, Protocall_Design, S&WIowegan, THE PILGRIM, Zarr, zzclancy |
09-07-2020, 03:09 AM
|
|
Member
|
|
|
Join Date: Jan 2011
Location: Badgerland
Posts: 2,373
Likes: 558
Liked 1,497 Times in 787 Posts
|
|
Here are pictures of both kinds of triggers (696 and 696-1).
Once you see these it's pretty obvious on other S&W revolvers.
The MIM case hardening colors can look just like the forged parts.
It's the same basic alloy, just assembled differently.
__________________
NEMO
"Everything 44"
Last edited by Nemo288; 09-07-2020 at 03:51 AM.
|
The Following 7 Users Like Post:
|
|
09-07-2020, 04:00 AM
|
|
Member
|
|
|
Join Date: Dec 2012
Location: (outside) Charleston, SC
Posts: 30,986
Likes: 41,646
Liked 29,239 Times in 13,823 Posts
|
|
Do they case harden...
Do they case harden MIM parts? I look for a light grey surface in case hardening.
__________________
"He was kinda funny lookin'"
|
09-07-2020, 06:43 AM
|
|
Member
|
|
|
Join Date: Jan 2011
Location: Badgerland
Posts: 2,373
Likes: 558
Liked 1,497 Times in 787 Posts
|
|
I have to assume they are.
The look of the 2 triggers above is so similar and the function identical.
The alloys are very close so the heat treating will be as well.
You are going to want that trigger sear to be as hard as possible.
Once the colors of case hardening, which are only a few molecules thick, wear off you can get a finish that looks like a coin finish but is still hardened.
There are so many types of hardened finishes now I have quit trying to keep track as they all look somewhat similar except for the really colorful ones.
For instance I believe my Rizzini double rifle has a vacuum vapor/plasma deposition chromium nitride finish but it looks like any other chrome or coin finish I have seen.
Heck it doesn't look any different from some stainless steel either but is supposedly harder than just about anything except diamond.
I haven't tried scratching it to find out .
The Kuhnhausen 5th edition S&W shop manual has a lengthy rant at the end about how the MIM parts rust way worse than the old forged parts.
This would have been written about some of the first MIM parts.
I am not sure why that would be or even if it is true if the alloys are similar.
I keep any non-stainless parts lightly coated with some kind of protectant and have not had any problems with that.
Eezox is one I use lately even though it is quite pungent.
Previous ones have included RIG grease lightly applied by rag and then wiped off and some of the spray products.
__________________
NEMO
"Everything 44"
Last edited by Nemo288; 09-07-2020 at 06:56 AM.
|
09-07-2020, 08:33 AM
|
Member
|
|
|
Join Date: Nov 2005
Location: VA
Posts: 4,677
Likes: 1,449
Liked 4,514 Times in 1,933 Posts
|
|
Just look at the back of the trigger and if it is hollow, then it is MIM. Forget about colors and all of that because case coloring (I disagree with hardening because anything that thin cant be doing any hardening) can be colorful to gray.
__________________
S&W factory revolver armorer
|
09-07-2020, 08:42 AM
|
Member
|
|
|
Join Date: Sep 2018
Posts: 1,874
Likes: 2,254
Liked 2,958 Times in 1,101 Posts
|
|
Speaking on J-frames, I always wondered why my 642-1 trigger was so nicely rounded and felt so good, while my 637-1 trigger was sharper and had edges that bothered my finger after an extended session.
Turns out the 642 is MIM and the 637 forged. Do they mold "nicer" contouring into all the MIM's?
|
09-07-2020, 08:50 AM
|
|
Member
|
|
|
Join Date: Apr 2009
Posts: 6,315
Likes: 13,115
Liked 12,802 Times in 4,228 Posts
|
|
Quote:
Originally Posted by mikerjf
Turns out the 642 is MIM and the 637 forged. Do they mold "nicer" contouring into all the MIM's?
|
I'm no expert, but my understanding is that one of the reasons why MIM was popularized was because it required less final machining, i.e., more-or-less ready-to-install out of the mold, with little, if any, polishing or fitting required. Could be why your 642's trigger has smoother edges than your 637's trigger.
|
The Following User Likes This Post:
|
|
09-07-2020, 09:32 AM
|
|
Member
|
|
|
Join Date: Dec 2012
Location: Michigan
Posts: 1,482
Likes: 550
Liked 1,427 Times in 666 Posts
|
|
Quote:
Originally Posted by ContinentalOp
I'm no expert, but my understanding is that one of the reasons why MIM was popularized was because it required less final machining, i.e., more-or-less ready-to-install out of the mold, with little, if any, polishing or fitting required.
|
Or, as S-W put it, with MIM the precision machining has to be done one time, when the mold is made, vs. every part has to be machined.
The engineer part of me loves the way the MIM parts are designed, metal where it needs to be and not where it isn't.
|
The Following 2 Users Like Post:
|
|
09-07-2020, 10:14 AM
|
Member
|
|
|
Join Date: Apr 2007
Location: Virginia
Posts: 8,761
Likes: 19,486
Liked 11,854 Times in 5,384 Posts
|
|
Quote:
Originally Posted by ContinentalOp
I'm no expert, but my understanding is that one of the reasons why MIM was popularized was because it required less final machining, i.e., more-or-less ready-to-install out of the mold, with little, if any, polishing or fitting required. Could be why your 642's trigger has smoother edges than your 637's trigger.
|
MIM is a cost saving measure, the by-product is a more uniform surface from one part to another, as opposed to forged and machined parts that relied upon a sharp cutter for a smooth, uniform surface. Once a cutter dulls or the cutting blades get little nicks, the cut surface becomes less uniform and has tiny ridges, which leads to a gritty trigger pull.
__________________
VCDL, GOA, NRA
|
09-07-2020, 12:30 PM
|
Member
|
|
|
Join Date: Feb 2011
Location: North Texas
Posts: 418
Likes: 390
Liked 403 Times in 176 Posts
|
|
Most MIM parts that I've looked at have small round ejector pin witness marks. Usually a dead give away unless they've been polished or machined off.
|
The Following User Likes This Post:
|
|
09-07-2020, 05:05 PM
|
Member
|
|
|
Join Date: Nov 2007
Location: Houston, Texas
Posts: 979
Likes: 1,118
Liked 1,242 Times in 536 Posts
|
|
MIM?? Ugh!
Quote:
Originally Posted by shocker
Or, as S-W put it, with MIM the precision machining has to be done one time, when the mold is made, vs. every part has to be machined.
The engineer part of me loves the way the MIM parts are designed, metal where it needs to be and not where it isn't.
|
The engineer in me appreciates the cost reduction that can be achieved with parts that are appropriate candidates for MIM. I do not like the way it looks. You can always see the graininess of the molded and sintered product unless it has been machined. Forged parts are so rough out out of the dies that nearly all surfaces have to be machined or ground to a pleasing polished look. Forged parts have one metallurgical advantage in that grain structure orientation can be optimized for loading. Not so with MIM. MIM has come a long way and is now the near equal of forged parts in fracture toughness, but nothing beats the beauty of a forged, machined and case hardened part. I like MIM stuff buried inside the gun where it can't be seen. In my shooting experience I have broken one MIM part, a old Taurus 92 hammer. Still waiting on my first forged part failure.
|
The Following User Likes This Post:
|
|
09-07-2020, 06:51 PM
|
|
Member
|
|
|
Join Date: Jan 2011
Location: Badgerland
Posts: 2,373
Likes: 558
Liked 1,497 Times in 787 Posts
|
|
Quote:
Originally Posted by Rocket3
Most MIM parts that I've looked at have small round ejector pin witness marks. Usually a dead give away unless they've been polished or machined off.
|
In the pictures I posted you can see at the top where the MIM trigger enters the frame, a round mark that may be where the sprue pin was cut off.
Quote:
Originally Posted by ken158
Forget about colors and all of that because case coloring (I disagree with hardening because anything that thin cant be doing any hardening) can be colorful to gray.
|
Case hardening need not involve a colored surface and the colors are not the hardened part.
The colors are a by product of certain methods of carburizing.
Case-hardening - Wikipedia
I have to believe that the hammer and trigger at least where they meet at the sear are hardened otherwise they would rapidly wear out.
Probably easier to just harden the whole part as indicated by the discoloring.
Hardening also reduces the friction.
The hardened layer can be up a mm thick.
When there are colors they are just sitting on the surface.
Color Case Hardening - Turnbull Restoration
Color Case Hardening - Shooting Sportsman Magazine
Goes into detail how Purdey case-hardens in colors their guns. Quite interesting.
"Jonathan Irby, James Purdey & Sons’ gunroom manager, offered this: “The color finish was—and is—the by-product of the hardening process. This is favored as providing a hard surface with a certain level of flex underneath, rather than a glass-hard finish.” Hardening incorporates carbon into the molecular structure of the surface steel and occurs when hot steel is splashed into cold water. The process gives the outer steel an armored skin that prevents wear and corrosion while preserving the interior, ductile, shock-absorbing strength."
Next they describe bone charcoal color case hardening.
"The colors themselves are perishable from sunlight and wear. The remaining colors on vintage guns offer a “rule of thumb” indication of cosmetic condition. Rubbing, wear and wiping can result in fading. This fading is varied and occurs first along edges."
It does not effect the hardening.
__________________
NEMO
"Everything 44"
Last edited by Nemo288; 09-07-2020 at 07:23 PM.
|
The Following User Likes This Post:
|
|
09-13-2020, 08:07 PM
|
Member
|
|
|
Join Date: Aug 2009
Location: Seattle
Posts: 3,422
Likes: 1,000
Liked 3,595 Times in 1,521 Posts
|
|
MIM parts are the same hardness al the way through. VERY hard wearing.
|
09-15-2020, 09:29 PM
|
US Veteran
|
|
|
Join Date: Feb 2005
Location: The SW Va Blue Ridge
Posts: 17,525
Likes: 89,698
Liked 24,883 Times in 8,520 Posts
|
|
"Still waiting on my first forged part failure."
Don't know if you would call it a "failure" or not, but I've replaced several J frame hammers after the revolvers have been dropped and landed on the hammer, snapping off the spur.
__________________
John 3:16
WAR EAGLE!
|
09-22-2020, 11:52 AM
|
Member
|
|
|
Join Date: Apr 2014
Location: MIchigan
Posts: 241
Likes: 92
Liked 191 Times in 83 Posts
|
|
You should be able to tell by the - number.
|
|